Typical physical properties
Typical physical properties
| Saturation polarization Js | 2.03 T |
| Coercive field strength Hc | 5A/m |
| Curie temperature Tc | 745 °C/1345 °F |
| Density Pm | 7.65 kg/dm3 |
| Electrical resistivity Pe | 0.48 µΩm |
| ULTIMATE TENSILE STRENGTH Rm | |
|---|---|
| ongitudinal in rolling direction | 330 - 370 MPa |
| transverse to rolling direction | 390 - 420 MPa |
| YIELD POINT Rp 0,2 | |
|---|---|
| longitudinal in rolling direction | 300 - 340 MPa |
| transverse to rolling direction | 330 - 360 MPa |
| ELONGATION Al=80 | |
|---|---|
| longitudinal in rolling direction | 6 - 14 % |
| transverse to rolling direction | 24 - 48 % |
| HARDNESS | |
|---|---|
| HRB 15T | 75 - 85 |
| HV5 | 170 - 195 |
| STACKING FACTOR, THICKNESS | |
|---|---|
| 0.23 mm | 95.5 % |
| 0.27 mm | 96.0 % |
| 0.30 mm | 96.5 % |
| 0.35 mm | 97.0 % |
* Plus tolerances must be specially agreed when ordering.